1. Instruction
Polyphenylene sulfide (PPS resin) is an organic polymer consisting of aromatic rings linked with sulfides. Synthetic fiber and textiles derived from this polymer are known to resist chemical and thermal attack. PPS is used to make filter fabric forcoal boilers, papermaking felts, electrical insulation, specialty membranes,gaskets, and packings.
2. Advantage
Advantage | Competitive price,high quality,on-time delivery,free sample |
Environment friendly | |
High Heat Resistance,High impact resistance | |
Without any impurity | |
Can be reinforced with the glass fiber from 30% to 70%. |
3. Tech parameters:
Property | Test Method | Units | Fiberglass Reinforced | |||||
P130T | P130T-04 | P140T | P140T-02 | P140T-04 | ||||
Physical | Density | ISO 1183 | g/cm3 | 1.56 | 1.56 | 1.65 | 1.65 | 1.65 |
Water Absorption | ISO 62 | % | 0.02 | 0.02 | 0.02 | 0.02 | 0.02 | |
MD/TD* | - | % | 0.4/0.7 | 0.4/0.7 | 0.3/0.6 | 0.3/0.6 | 0.3/0.6 | |
Mechanical | Tensile Strength | ISO 527 | MPa | 150 | 145 | 185 | 180 | 175 |
Elongation at Break | ISO 527 | % | 3.0 | 6.0 | 2.0 | 4.0 | 4.0 | |
Flexural Strength | ISO 178 | MPa | 220 | 210 | 260 | 250 | 250 | |
Flexural Modulus | ISO 178 | GPa | 11.0 | 8.0 | 13.0 | 12.0 | 11.5 | |
Impact Strength | ISO 180 | kJ/m2 | 10.0 | 12.0 | 12.0 | 14.0 | 15.0 | |
Rockwell Hardness | ISO 2039/2 | R scale | 120 | 120 | 120 | 120 | 120 | |
Thermal | Heat Deflection Temperature | ISO 75 | °C | 265 | 265 | 265 | 265 | 265 |
Flammability Rating | UL-94 | - | V0 | V0 | V0 | V0 | V0 | |
Electrical | Volume Resistivity | ISO 167 | Ohm.cm | 5×1016 | 5×1016 | 5×1016 | 5×1016 | 5×1016 |
Dielectric Strength | ASTM D149 | KV/mm | 16 | 16 | 16 | 16 | 16 | |
Dielectric Constant | ASTM D150 | - | 3.6 | 3.6 | 3.8 | 3.8 | 3.8 | |
Wastage Factor | ASTM D150 | - | 0.002 | 0.002 | 0.002 | 0.002 | 0.002 | |
Process Conditions | Injection Temperature | - | °C | 290~330 | 290~330 | 290~330 | 290~330 | 290~330 |
Mold Temperature | - | °C | 120~150 | 120~150 | 120~150 | 120~150 | 120~150 | |
* MD: Mold direction; TD: Transverse direction | ||||||||